New material for solid oxide fuel cells

Higher conductivity and lower coefficient of thermal expansion

26-Jul-2018 - Russian Federation

Scientists have replaced some of the iron atoms in the composition Nd0.5Ba0.5FeO3-δ by cobalt, while simultaneously increasing the conductivity and lowering the thermal expansion of the material.

To improve conductivity through the change in the number of defects as a starting point for the study, scientists took mixed ferrite neodym and barium Nd0.5Ba0.5FeO3-δ.

To replace part of the iron, cobalt (Co), copper (Cu) and nickel (Ni) were added to the starting material. Complex oxides were obtained by evaporation of solutions and calcination of the solid residue at a temperature of 700 degrees Celsius. The thermal expansion of all mixed materials turned out to be weaker than that of the original Nd0.5Ba0.5FeO3-δ, which includes up to ten percent of the doping metals. To improve the thermal expansion, the material with copper was the best, and in the case of ionic conductivity, the best was cobalt.

A group of scientists from UrFU and Institute of High-Temperature Electrochemistry (Ural Division of the Russian Academy of Science), achieved a balance between good conductive properties and the absence of thermal expansion using cobalt.

Original publication

Other news from the department science

These products might interest you

Multi-Liter Hydrogen Gasgenerator

Multi-Liter Hydrogen Gasgenerator by VICI

Laboratory hydrogen supply redefined

Up to 18 l/min hydrogen with 99.99997% purity and intuitive touchscreen control

hydrogen generators
CATLAB Catalysis and Thermal Analysis

CATLAB Catalysis and Thermal Analysis by Hiden Analytical

A system for catalyst characterisation, kinetic and thermodynamic measurements

Integrated Microreactor-Mass Spectrometer for Reaction Testing, TPD/R/O and Pulse Chemisorption.

mass spectrometers
Loading...

Most read news

More news from our other portals

All FT-IR spectrometer manufacturers at a glance