Diamond-like carbon

Diamond-like carbon (DLC) is any of seven forms^[1] of amorphous carbon materials that display some of the unique properties of natural diamond. They are usually applied as coatings to other materials that could benefit from some of those properties. All seven contain significant amounts of sp³ hybridized carbon atoms. The reason that there are different types is that even natural diamond can be found in two crystalline polytypes. The usual one has its carbon atoms arranged in a cubic lattice, while the very rare one (lonsdaleite) has a hexagonal lattice. By mixing these polytypes in various ways at the nanoscale level of structure, DLC coatings can be made that at the same time are amorphous, flexible, and yet purely sp³ bonded "diamond". The hardest, strongest, and slickest is such a mixture, known as tetrahedral amorphous carbon, or ta-C. For example a coating of only 2μm thickness of ta-C increases the resistance of common (i.e. type 304) stainless steel against abrasive wear; changing its lifetime in such service from one week to 85 years. Such ta-C can be considered to be the "pure" form of DLC, since it consists only of sp³ bonded carbon atoms. Fillers such as hydrogen, graphitic sp² carbon, and metals are used in the other 6 forms to reduce production expenses, but at the cost of decreasing the service lifetimes of the articles being coated. The various forms of DLC can be applied to almost any material that is compatible with a vacuum environment. In 2006, the market for outsourced DLC coatings was estimated to be about 30,000,000 € in the EU.

Additional recommended knowledge

What is the Correct Way to Check Repeatability in Balances?

How to ensure accurate weighing results every day?

Correct Test Weight Handling Guide: 12 Practical Tips

Distinction from natural and synthetic diamond

Naturally occurring diamond is almost always found in the crystalline form with a purely cubic orientation of sp³ bonded carbon atoms. Sometimes there are lattice defects or inclusions of atoms of other elements that give color to the stone, but the lattice arrangement of the carbons remains cubic and bonding is purely sp³. The internal energy of the cubic polytype is slightly lower than that of the hexagonal form and growth rates from molten material in both natural and bulk synthetic diamond production methods are slow enough that the lattice structure has time to grow in the lowest energy (cubic) form that is possible for sp³ bonding of carbon atoms. In contrast, DLC is typically produced by processes in which high energy precursive carbons (e.g. in plasmas, in sputter deposition and in ion beam deposition) are rapidly cooled or quenched on relatively cold surfaces. In those cases cubic and hexagonal lattices can be randomly intermixed, layer by atomic layer, because there is no time available for one of the crystalline geometries to grow at the expense of the other before the atoms are "frozen" in place in the material. Amorphous DLC coatings can result that have no long range crystalline order. Without long range order there are no brittle fracture planes, so such coatings are flexible and conformal to the underlying shape being coated, while still being as hard as diamond.

Production

 There are several methods for producing DLC, but all depend upon the fact that in carbon the sp³ bond length is significantly less than the length of the sp² bond. So the application of pressure, impact, catalysis, or some combination of these at the atomic scale can force sp² bonded carbon atoms closer together into sp³ bonds. This must be done vigorously enough that the atoms cannot simply spring back apart into separations characteristic of sp² bonds. Usually techniques either combine such a compression with a push of the new cluster of sp³ bonded carbon deeper into the coating so that there is no room for expansion back to separations needed for sp² bonding; or the new cluster is buried by the arrival of new carbon destined for the next cycle of impacts. It is reasonable to envision the process as a "hail" of projectiles that produce localized, faster, nanoscale versions of the classic combinations of heat and pressure that produce natural and synthetic diamond. Because they occur independently at many places across the surface of a growing film or coating, they tend to produce an analog of a cobblestone street with the cobbles being nodules or clusters of sp³ bonded carbon. Depending upon the particular "recipe" being used, there are cycles of deposition of carbon and impact or continuous proportions of new carbon arriving and projectiles conveying the impacts needed to force the formation of the sp³ bonds. As a result, ta-C may have the structure of a cobblestone street, or the nodules may "melt together" to make something more like a sponge or the cobbles may be so small as to be nearly invisible to imaging. A classic "medium" morphology for a ta-C film is shown in the figure.

Properties

These [sp³] bonds can occur not only with crystals - in other words, in solids with long-range order - but also in amorphous solids where the atoms are in a random arrangement. In this case there will be bonding only between a few individual atoms and not in a long-range order extending over a large number of atoms. The bond types have a considerable influence on the material properties of amorphous carbon films. If the sp² type is predominant the film will be softer, if the sp³ type is predominant the film will be harder.

Hardness

Within the "cobblestones", nodules, clusters, or "sponges" (the volumes in which local bonding is sp³) bond angles may be distorted from those found in either pure cubic or hexagonal lattices because of intermixing of the two. The result is internal (compressive) stress that can appear to add to the hardness measured for a sample of DLC. Hardness is often measured by nanoindentation methods in which a finely pointed stylus of natural diamond is forced into the surface of a specimen. If the sample is so thin that there is only a single layer of nodules, then the stylus may enter the DLC layer between the hard cobblestones and push them apart without sensing the hardness of the sp³ bonded volumes. Measurements would be low. Conversely, if the probing stylus enters a film thick enough to have several layers of nodules so it cannot be spread laterally, or if it enters on top of a cobblestone in a single layer, then it will measure not only the real hardness of the diamond bonding, but an apparent hardness even greater because the internal compressive stress in those nodules would provide further resistance to penetration of the material by the stylus. Nanoindentation measurements have reported hardness as great as 50% more than values for natural crystalline diamond. Since the stylus is blunted in such cases or even broken, actual numbers for hardness that exceed that of natural diamond are meaningless. They only show that the hard parts of an optimal ta-C material will break natural diamond rather than the inverse. Nevertheless, from a practical viewpoint it does not matter how the resistance of a DLC material is developed, it can be harder than natural diamond in usage.  

Bonding of DLC coatings

The same internal stress that benefits the hardness of DLC materials makes it difficult to bond such coatings to the substrates to be protected. The internal stresses try to "pop" the DLC coatings off of the underlying samples. This challenging downside of extreme hardness is answered in several ways, depending upon the particular "art" of the production process. The most simple is to exploit the natural chemical bonding that happens in cases in which incident carbon ions supply the material to be impacted into sp³ bonded carbon atoms and the impacting energies that are compressing carbon volumes condensed earlier. In this case the first carbon ions will impact the surface of the item to be coated. If that item is made of a carbide-forming substance such as Ti or Fe in steel a layer of carbide will be formed that is later bonded to the DLC grown on top of it. Other methods of bonding include such strategies as depositing intermediate layers that have atomic spacings that grade from those of the substrate to those characteristic of sp³ bonded carbon. In 2006 there were as many successful recipes for bonding DLC coatings as there were sources of DLC.

Tribology

DLC coatings are often used to prevent wear due to its excellent tribological properties. DLC is very resistant to abrasive and adhesive wear making it suitable for use in applications that experience extreme contact pressure, both in rolling and sliding contact. DLC is often used to prevent wear on razor blades and metal cutting tools, including lathe inserts and milling cutters. DLC is used in bearings, cams, cam followers, and shafts in the automobile industry. The coatings reduce wear during the 'break-in' period, where drive train components may be starved for lubrication.

DLC's may also be used in chameleon coatings that are designed to prevent wear during launch, orbit, and re-entry of land launched space vehicles. DLC provides lubricity at ambient atmosphere and at vacuum, unlike graphite which requires moisture to be lubricious.

Despite the favorable tribological properties of DLC it must be used with caution on ferrous metals. If it is used at higher temperatures, the substrate or counter face may carburize, which could lead to loss of function due to a change in hardness. This phenomenon prevents the use of DLC coated machine tool on steel.

Electrical

If a DLC material is close enough to ta-C on plots of bonding ratios and hydrogen content it can be an insulator with a high value of resistivity. Perhaps more interesting is that if prepared in the "medium" cobblestone version such as shown in the above figure, electricity is passed through it by a mechanism of hopping conductivity that is unfortunately not covered in the Wikipedia reference on the topic. In this type of conduction of electricity the electrons move by quantum mechanical tunneling between pockets of conductive material isolated in an insulator. The result is that such a process makes the material something like a semiconductor. Further research on electrical properties is needed to explicate such conductivity in ta-C in order to determine its practical value. However, a different electrical property of emissivity has been shown to occur at unique levels for ta-C. Such high values allow for electrons to be emitted from ta-C coated electrodes into vacuum or into other solids with application of modest levels of applied voltage. This has supported important advances in medical technology.

Applications

By 2007 the most prevalent applications of DLC were those exploiting the ability of this material to reduce abrasive wear especially for tools (milling, drilling), stamps and moulds^[3]. For example, DLC is used in the engines of most modern supersport motorcycles, Formula 1 racecars^[4], NASCAR vehicles, and is used as a coating on hard-disk platters and hard-disk read heads to protect against head crashes. Virtually all of the multi-bladed razors used for wet shaving have the edges coated with hydrogen-free DLC to reduce abrasion of sensitive skin. Some forms have been certified in the EU for food service and find extensive uses in the high-speed actions involved in processing novelty foods such as "chips" and in guiding material flows in packaging foodstuffs with plastic wraps. DLC coats the cutting edges of tools for the high-speed, dry shaping of difficult exposed surfaces of wood and aluminum, for example on automobile dashboards.

The implantable human heart pump^[5] can be considered the ultimate biomedical application where DLC coating is used on blood contacting surfaces of the key components of the device.

Other medical applications such as Percutaneous coronary intervention employing brachytherapy find additional benefits from the unique electrical properities of DLC. At low voltages and low temperatures electrodes coated with DLC can emit enough electrons to be arranged into disposable, micro-X-ray tubes as small as the radioactive seeds that are introduced into arteries or tumors in conventional brachytherapy. The same dose of prescribed radiation can be applied from the inside, out with the additional possibility to switch on and off the radiation in the prescribed pattern for the X-rays being used.

Societal concerns, impact on the sustainable economy

Peer-reviewed research published in scholarly journals has established that the increases in lifetimes of articles coated with DLC that wear out because of abrasion can be described by the formula , where g is a number that characterizes the type of DLC, the type of abrasion, the substrate material and μ is the thickness of the DLC coating in μm.^[6] For "low-impact" abrasion (pistons in cylinders, impellers in pumps for sandy liquids, etc.), g for pure ta-C on 304 stainless steel is 66. This means that one-μm thickness (i.e. ~5% of the thickness of a human hairend) would increase service lifetime for the article it coated from a week to over a year and two-μm thickness would increase it from a week to 85 years. These are measured values; though in the case of the 2μm coating the lifetime was extrapolated from the last time the sample was evaluated until the testing apparatus itself wore out.

In a global sense, environmental concerns prove the needs for a sustainable economy in which articles are not engineered to lower performance or to fail prematurely in order to support greater production of units and their frequent replacements. Yet there are about 100 outsource vendors of DLC coatings that are loaded with amounts of graphite and hydrogen and so give much lower g-numbers than 66 on the same substrates. In 2007 an availability of the more durable forms began to appear.^[7]

See also

• Chemical vapor deposition
• Cathodic arc deposition

References

1. ^ http://www.ist.fraunhofer.de/english/c-products/tab/complete.html
2. ^ http://www.vdi.de/vdi/presse/mitteilungen_details/index.php?ID=1015889
3. ^ http://www.argor-aljba.com
4. ^ http://www.bekaert.com/bac/Products/Diamond-like%20coatings/Racing%20Engine%20Parts.htm
5. ^ http://www.ventracor.com/ventrassist/ventassist_productpr.asp
6. ^ C.B. Collins, F. Davanloo, et al. J. Vac. Sci. Technol. B,11, 1936 (1993)
7. ^ Links to sources of pure DLC.