Evaporation (deposition)

  Evaporation is a common method of thin film deposition. The source material is evaporated in a vacuum. The vacuum allows vapor particles to travel directly to the target object (substrate), where they condense back to a solid state. Evaporation is used in microfabrication, and to make macro-scale products such as metallized plastic film.

Additional recommended knowledge

Safe Weighing Range Ensures Accurate Results

Better weighing performance in 6 easy steps

How to ensure accurate weighing results every day?

Physical principle

  Evaporation involves two basic processes: a hot source material evaporates and condenses on the substrate. It resembles the familiar process by which liquid water appears on the lid of a boiling pot. However, the gaseous environment and heat source (see "Equipment" below) are different.

Evaporation takes place in a vacuum, i.e. vapors other than the source material are almost entirely removed before the process begins. In high vacuum (with a long mean free path), evaporated particles can travel directly to the deposition target without colliding with the background gas. (By contrast, in the boiling pot example, the water vapor pushes the air out of the pot before it can reach the lid.) At a typical pressure of 10^-4 Pa, an 0.4-nm particle has a mean free path of 60 m. Hot objects in the evaporation chamber, such as heating filaments, produce unwanted vapors that limit the quality of the vacuum.

Evaporated atoms that collide with foreign particles may react with them; for instance, if aluminium is deposited in the presence of oxygen, it will form aluminium oxide. They also reduce the amount of vapor that reaches the substrate, which makes the thickness difficult to control.

Evaporated materials deposit nonuniformly if the substrate has a rough surface (as integrated circuits often do). Because the evaporated material attacks the substrate mostly from a single direction, protruding features block the evaporated material from some areas. This phenomenon is called "shadowing" or "step coverage."

When evaporation is performed in poor vacuum or close to atmospheric pressure, the resulting deposition is generally non-uniform and tends not to be a continuous or smooth film. Rather, the deposition will appear fuzzy or cloudy.

Equipment

Any evaporation system includes a vacuum pump. It also includes an energy source that evaporates the material to be deposited. Many different energy sources exist:

• In the thermal method, the source material is placed in a crucible, which is radiatively heated by an electric filament. Alternatively, the source material may be hung from the filament itself (filament evaporation).
  • Molecular beam epitaxy is an advanced form of thermal evaporation.
• In the electron-beam method, the source is heated by an electron beam with an energy up to 15 keV. See Electron beam evaporation.
• In flash evaporation, a fine wire of source material is fed continuously onto a hot ceramic bar, and evaporates on contact.
• Resistive evaporation is accomplished by passing a large current through a wire or foil of the material that is to be deposited.

Some systems mount the substrate on an out-of-plane planetary mechanism. The mechanism rotates the substrate simultaneously around two axes, to reduce shadowing.

Optimization

 Evaporation systems may be judged by the following qualities:

• Purity of the deposited film depends on the quality of the vacuum, and on the purity of the source material.
• The thickness of the film will vary due to the geometry of the evaporation chamber. Collisions with residual gases aggravate nonuniformity of thickness.
• Filament and resistive evaporation cannot deposit thick films, because the size of the filament limits the amount of material that can be deposited. However, flash evaporation and methods that use crucibles can deposit thick films.
• In order to deposit a material, the evaporation system must be able to melt it. This makes refractory materials such as tungsten hard to deposit by methods that do not use electron-beam heating.
• Electron-beam evaporation allows tight control of the evaporation rate. Thus, an electron-beam system with multiple beams and multiple sources can deposit a chemical compound or composite material of known composition.
• Step coverage

Applications

An important example of an evaporative process is the production of aluminized PET film packaging film in a roll-to-roll web system. Often, the aluminum layer in this material is not thick enough to be entirely opaque since a thinner layer can be deposited more cheaply than a thick one. The main purpose of the aluminum is to isolate the product from the external environment by creating a barrier to the passage of light, oxygen, or water vapor.

Evaporation is commonly used in microfabrication to deposit metal films.

Comparison to other deposition methods

• Alternatives to evaporation, such as sputtering and chemical vapor deposition, have better step coverage. This may be an advantage or disadvantage, depending on the desired result.
• Sputtering tends to deposit material more slowly than evaporation.
• Sputtering uses a plasma, which produces many high-speed atoms that bombard the substrate and may damage it. Evaporated atoms have a Maxwellian energy distribution, determined by the temperature of the source, which reduces the number of high-speed atoms. However, electron beams tend to produce X-rays (Bremsstrahlung) and stray electrons, each of which can also damage the substrate.